| LEGHE AUSTENITICHE |
Designazione |
|||||
ACI/ASTM |
DIN |
AFNOR |
UNS |
Altre |
|
CF20 |
A743 CF20 |
1.4312 GX10CrNi188 |
Z10CN18.9M |
- |
- |
CF8 |
A351 CF8 |
1.4308 GX6CrNi189 |
Z6CN18.10M |
J92600 |
AISI 304 (5) |
CF8A |
A351 CF8A |
- |
- |
J92600 |
AISI 304H (5) |
CF8C |
A351 CF8C |
1.4552 GX5CrNiNb189 |
Z6CNNb18.10M |
J92910 |
AISI 347 (5) |
CF3 |
A351 CF3 |
1.4306 X2CrNi1911 (5) |
Z2CN18.10M |
J92500 |
AISI 304L (5) |
CF3A |
A351 CF3A |
- |
- |
J92500 |
- |
CF8M |
A351 CF8M |
1.4408 GX6CrNiMo1810 |
Z6CND18.12M |
J92900 |
AISI 316 (5) |
CF8MNb |
A351 CF10MC |
1.4851 GX5CrNiMoNb1810 |
Z6CNDNb18.12M |
- |
AISI 316Nb (5) |
CF3M |
A351 CF3M |
1.4404 X2CrNiMo17122 (5) |
Z2CND18.12M |
J92800 |
AISI 316L (5) |
CF3MS |
AISI316LS (5) |
1.4435 X2CrNiMo18143 (5) |
- |
- |
AISI 316LS (5) |
CF3MN |
A351 CF3MN |
- |
- |
- |
AISI 316LN (5) |
CF16F |
A743 CF16F |
- |
- |
J92701 |
AISI 303 (5) |
CG8M |
A351 CG8M |
- |
- |
J93000 |
AISI 317 (5) |
1.4439 |
- |
1.4439 GX3CrNiMoN17135 |
- |
- |
- |
CK20 |
A351 CK20 |
- |
- |
J94202 |
AISI 310S (5) |
316HP |
- |
- |
- |
- |
(6) |
316LHP |
- |
- |
- |
- |
(6) |
Composizione chimica |
||||||||
C |
Cr |
Ni
|
Mo
|
Altri
|
Trattamento termico (1)
|
Microstruttura (2)
|
||
CF20
|
< 0.20 |
19.5 |
9.5
|
-
|
-
|
S
|
a
|
|
CF8 |
< 0.08 |
19.5 |
9.5 |
< 0.5 |
- |
S |
a, (f) |
|
CF8A |
< 0.08 |
19.5 |
9.5 |
< 0.5 |
- |
S |
a, (f) |
|
CF8C |
< 0.08 |
19.5 |
10.5 |
< 0.5 |
Nb>8x%C |
S |
a, (f) |
|
CF3 |
< 0.03 |
19.0 |
10.0 |
< 0.5 |
- |
S |
a, (f) |
|
CF3A |
< 0.03 |
19.0 |
10.0 |
< 0.5 |
- |
S |
a, (f) |
|
CF8M |
< 0.08 |
19.5 |
10.5 |
2.3 |
- |
S |
a, (f) |
|
CF8MNb |
< 0.08 |
19.5 |
10.5 |
2.3 |
Nb>8x%C |
S |
a, (f) |
|
CF3M |
< 0.03 |
19.0 |
11.0 |
2.3 |
- |
S |
a, (f) |
|
CF3MS |
< 0.03 |
19.0 |
13.5 |
2.7 |
- |
S |
a |
|
CF3MN |
< 0.03 |
19.0 |
11.0 |
2.3 |
0.15N |
S |
a |
|
CF16F |
< 0.16 |
19.5 |
10.5 |
< 1.5 |
S, (P), (Se) |
S |
a, (f, i) |
|
CG8M |
< 0.08 |
19.5 |
11.0 |
3.5 |
- |
S |
a |
|
1.4439 |
< 0.03 |
17.5 |
13.5 |
4.5 |
0.17N |
S |
a |
|
CK20 |
< 0.20 |
20.0 |
20.5 |
< 0.5 |
- |
S |
a |
|
316HP |
< 0.07 |
21.0 |
9.0 |
2.3 |
0.12N |
S |
a, (f) |
|
316LHP |
< 0.03 |
21.0 |
9.0 |
2.3 |
0.12N |
S |
a, (f) |
|
Proprietà meccaniche e fisiche |
||||||||
Limite elastico 0.2% MPa min. |
Rottura MPa min. |
Allungamento %min. |
Durezza HB (3) |
Resilienza KV J (3) |
Densità Kg/dm3 |
Ritiro lineare |
Saldabilità (4) |
|
CF20
|
205 |
485 |
30 |
150-200 |
80 |
7.75 |
2.7% |
1 |
CF8
|
205 |
485 |
35 |
140-200 |
120 |
7.75 |
2.6% |
1 |
CF8A
|
240 |
530 |
35 |
150-200 |
110 |
7.75 |
2.6% |
1 |
CF8C
|
205 |
485 |
30 |
140-200 |
80 |
7.75 |
2.7% |
1 |
CF3
|
205 |
485 |
35 |
140-200 |
140 |
7.75 |
2.6% |
1 |
CF3A
|
240 |
530 |
35 |
150-200 |
120 |
7.75 |
2.6% |
1 |
CF8M
|
205 |
485 |
30 |
140-200 |
120 |
7.75 |
2.6% |
1 |
CF8MNb
|
205 |
485 |
25 |
140-200 |
110 |
7.75 |
2.7% |
2 |
CF3M
|
205 |
485 |
30 |
140-200 |
120 |
7.75 |
2.6% |
1 |
CF3MS
|
205 |
485 |
25 |
140-200 |
120 |
7.75 |
2.6% |
1 |
CF3MN
|
255 |
515 |
35 |
150-200 |
140 |
7.75 |
2.6% |
1 |
CF16F
|
205 |
485 |
30 |
140-200 |
100 |
7.75 |
2.6% |
2 |
CG8M
|
240 |
515 |
25 |
150-200 |
100 |
7.75 |
2.6% |
1 |
1.4439
|
210 |
490 |
20 |
140-200 |
120 |
7.75 |
2.6% |
1 |
CK20
|
195 |
450 |
30 |
150-220 |
80 |
7.75 |
2.7% |
2 |
316HP
|
300 |
550 |
35 |
150-200 |
120 |
7.75 |
2.6% |
1 |
316LHP
|
300 |
550 |
35 |
150-200 |
120 |
7.75 |
2.6% |
1 |
| (1) A: Ricotto; N: Normalizzato e rinvenuto; H: Bonificato; S: Solubilizzato; P: Invecchiato per precipitazione; () Opzionale. | ||||||||
| (2) a: Austenite; f: Ferrite delta; m: Martensite; i: Fasi intermetalliche; (): Fase secondaria. |
||||||||
| (3) Valori tipici a 20° C. | ||||||||
| (4) 1: Molto buona; 2: Buona; 3: Discreta con precauzioni; 4: Generalmente scarsa. | ||||||||
| (5) Corrispondente laminato | ||||||||
| (6) Brevetto Fondinox. | ||||||||